Cross-sectional polishing service for implemented parts and electronic components.

We will introduce an example of the analysis of compounds formed at the interface between Sn-Ag-Cu solder and NiP pads. At the interface between the NiP pad and Sn-Ag-Cu solder, compounds such as (Ni,Cu)3Sn4 and (Cu,Ni)6Sn5 grow, and surface analysis using EDX reveals the distribution of Ni, Cu, and Sn within these compounds. The EBSD method is an analytical technique based on the crystallographic information of the sample. By combining it with elemental analysis using EDX, it is possible to estimate the composition, and in some cases, it may be feasible to analyze using the crystallographic data of Ni3Sn4 and Cu6Sn5 as substitutes.

In the methods for cross-section preparation in semiconductor structural observation and defect analysis, CP, FIB, and mechanical polishing are mentioned, each having its own advantages and disadvantages, making it necessary to consider which method to use. In recent years, CP and FIB have become more common, and it seems that the use of mechanical polishing, which requires technical skill, is decreasing. However, it is still not to be dismissed. While there are merits and demerits, it is possible to achieve cross-section preparation with mechanical polishing that is comparable to FIB and CP. At our company, based on years of accumulated know-how, we propose the most appropriate processing methods according to the observation purpose and the composition and structure of the samples.

We would like to introduce an example of cross-sectional observation of mounted components conducted by our company. Using commercially available computer circuit boards, we observed the solder joints of mounted components and the internal structures of the components using a metal microscope. The observation modes of the metal microscope include bright field observation, dark field observation, and polarized light observation, among others. Additionally, there are observations using transmitted light, and the observation mode is selected according to the sample. By conducting cross-sectional observations before and after reliability testing, we can evaluate the reliability of the product. When observing, it is important to select an appropriate "observation mode" to clearly capture the condition of the solder joint interface and defects such as cracks.

Here, we present examples of cross-sectional observations of various components mounted on a board known as an organic substrate. Inside various electronic devices around us, there are substrates equipped with electronic components. When observing the mounted substrates, you can see that numerous components are tightly soldered together. It is necessary to verify that these components are properly joined, as improper connections can lead to malfunction. Please contact us if you are considering observations before and after reliability testing or cross-sectional observations.