The specific wear rate was calculated using the mass loss method! A comparison of the specific wear rates for various material combinations was conducted.
We will introduce the friction and wear characteristics testing of laser cladding (ball-on-disk). Using a ball-on-disk type friction and wear testing machine, we measured the friction force and wear amount. The specific wear rate was calculated using the mass loss method, and a comparison of the specific wear rates for each material combination was conducted. For detailed information about the test, please download the catalog. 【Test Conditions】 ■ Lubrication: Dry (no lubrication) ■ Test Temperature: Room temperature ■ Ball: 3/8in, SUS440C, SUJ2 ■ Load: 9.8N (1kgf) ■ Friction Speed (Rotational Speed): 12.6m/min (400rpm) ■ Friction Time: 600sec *For more details, please refer to the PDF document or feel free to contact us.
Inquire About This Product
basic information
For more details, please refer to the PDF document or feel free to contact us.
Price range
Delivery Time
Applications/Examples of results
For more details, please refer to the PDF document or feel free to contact us.
catalog（2）
Download All Catalogs
Company information
Silicolloy is a revolutionary new material that contains a large amount of silicon (silicon) and was developed using pure domestic technology. Silicolloy is a super alloy that possesses high strength, heat resistance (high-temperature oxidation resistance), corrosion resistance, wear resistance, high hardness, and low dimensional changes during heat treatment, all in one steel. Currently, many engineers (technicians and designers) are advancing its commercialization, contributing to new product development and total cost reduction through increased longevity. There is 'Silicolloy A2', which excels in overall balance as a precipitation-hardened stainless steel, and 'Silicolloy XVI', which has the highest hardness in the world as a precipitation-hardened type. Those who require both corrosion resistance and high hardness should not miss it!